This article makes a microstructural characterization of the transformations that occur in a dissimilar weld, by means of a gas and tungsten welding process, between the B 521 tantalum alloy and the AISI 316 stainless steel. The seam was made butt, in pipes 1.3 millimeters thick, with a non-consumable 2% thorium tungsten electrode (WT20). The parameters of the thermal cycle considered were the welding speed, the linear and incoming energy of the process. In this union, due to the effect of heat transfer, a coarse columnar type of structure, dendritic structures, as well as a structure of a network of hexagonal cells and δ-ferrite were generated. In the hardness sweep, an increase of the same in the zone affected by the heat of 200 HV was determined in the first (Tantalum) and of 285 HV for the second (stainless steel), with a value of 525 HV in the molten zone.En este artículo se hace una caracterización microestructural de las transformaciones que ocurren en una soldadura disímil, mediante el proceso de soldadura de gas y tungsteno, entre la aleación de tantalio B 521 y el acero inoxidable AISI 316. La costura se realizó a tope, en tuberías de 1,3 milímetros de espesor, con electrodo no consumible de tungsteno al 2 % de torio (WT20). Los parámetros del ciclo térmico considerados fueron la velocidad de soldadura, la energía lineal y entrante del proceso. En esta unión, por efecto de la transferencia de calor, se generó estructura del tipo columnas tosca, estructuras dendríticas, así como una estructura de una red de células hexagonales y ferrita-δ. En el barrido de dureza se determinó un incremento en la zona afectada por el calor de 200 HV en el primero (Tantalio) y de 285 HV para el segundo (acero inoxidable), con un valor de 525 HV en la zona fundida.